Bopet Plain Film

Category: BOPET Film Clear transparent

BOPET PLAIN FILM
BOPET film (biaxially oriented Polyester films) featurines good thermal stability and tenacity; low air and water permeability; applicable to vacuum aluminum plating, compound package, cooking bag manufacture, etc.
Biaxially-oriented polyester (BOPET) plain film with good thermal stability, tenacity and low air/water permeability, suitable for vacuum aluminium plating, composite packaging and cooking-bag manufacture. Good ink and coating adhesion supports multi-colour printing, and it's commonly used for heat-sealed bags in frozen food, industrial goods and cosmetics packaging.
Featuring :
Having the good adhesion with ink and coating, can be used for multi-color printings with good flatness. Is mainly used in heat-sealing bags of frozen food, industrial products and cosmetics packaging.
Specification:
thickness: 12 microns-25 microns, 75 microns-150 microns ,185 microns-380 microns, 500 microns
width :200-1200MM
length : 500m ,1000m ,1500m,4000m,6000m,9000m,12000m
Polyester film is wound around paper shaft with an internal diameter of 76.2mm-152.4mm and covered with polyethylene film; each coil is supported by damper and put in carton; medium and large package needs wooden mount.
Customer's own requirement is available for us such as printed OEM logos and private label or particular size and package style.

Thickness: 12-25 / 75-150 / 185-380 / 500 micron

Polyester Film Test Report

Film Item		BOPET		Date		Quantity	2,841tons
Roll NO.		B--07121704		Test Date		Temperature/Humidity Condition		23℃/50RH
Test Criterion		《Polyester testing method》Thickness :14um
No.	Item			Unit	Average	Standard Deviation		Remarks
1	Average Thickness/Thickness Tolerance			ΜM	14.2	0.17		Average Thickness Tolerance: +1.7%
				%	Min.: -1.9	Max:+1.9
2	Tensile Strength		MD	Mpa	235	10
			TD		268	35
3	Elongation		MD	%	130	13
			TD		113	12
4	Heat Shrinkage		MD	%	1.7	0.2		Temperature:150℃ Time:30min
			TD		-0.1	0.1
5	Haze			%	2.3	0.1
6	1.2 Glossy							45°
7	COF		ΜS		1.41	0.03		Opposite Surface :F/F
			ΜK		1.38	0.01
			ΜS					Same Surface :F/F
			ΜK
8	Modul		MD	M Pa	4474	122
			TD		4914	308
9	Humid Tension			M N/M	58
10	Hot-Sealing Strength			N/15mm				1bar/130℃/1s
11	Relative Dielectric Constant（50Hz）
12	Dielectric Dissipation Factor（50Hz）			Pp M
13	Dielectric Strength			V/ΜM
14	Volume Resistivity			ΩCm